Laboratory small wear resistant high temperature zirconia ball grinding tank
Description:
Zirconia ball grinding tank can be widely used in precious metal materials, electronic materials, color coatings, magnetic materials, and other industries. Using reasonable and unique tank mouth tooling seal, easy sealing, tight sealing, beautiful appearance, strong and durable. In use, there will be no gap leakage, storage dead Angle and other undesirable phenomena, can be processed in a short time to narrow fineness distribution of ultrafine materials.
Principal characteristic of Were resistance thread hole zirconia ceramic stirring head for sand mill &ball mill:
1 High wall finish, not easy to stick material.
2. Strong oxidation resistance, acid and alkali resistance.
3. Excellent corrosion resistance
4. Good intergranular corrosion resistance
5. High temperature resistance is also better.
6. High wear resistance and long service life.
7. High grinding efficiency.
Application of were resistance thread hole zirconia ceramic stirring head for sand mill &ball mill:
Ultrafine grinding equipment, fine chemical industry, electronic paste, semiconductor, new energy, nano new materials, medical instruments, precision casting, structural ceramics, refractory materials, electronic communications, sensitive ceramics, petrochemical industry, aerospace, machinery manufacturing, optical fiber connector, battery materials and other high-precision end fields
Technical Parameters:
| Specification | Outer diameter | inner diameter | Bottom diameter | Height | Cover thickness |
| 50ML | 64 | 50 | 64 | 56 | 12 |
| 100ML | 74 | 60 | 64 | 68 | 12 |
| 250ML | 94 | 80 | 89.5 | 88 | 13 |
| 500ML | 103 | 89 | 89.5 | 100 | 13 |
| 1L | 130 | 114 | 119.5 | 118 | 13 |
| TIPS:The size list is for reference only, the above is the standard size of conventional products,specialspecifications can be customized . |
| Item | unit | Typical Values |
| Composition | (wt%) | 94.8%ZrO2+5.2%Y2O3(wt%) |
| Color | - | White |
| Density | g/cm3 | 6.03 |
| Water absorption | ％ | 0 |
| flexure strength | MPa | 1250 |
| HV hardness | GPa | 1300 |
| Modulus of Elasticity | GPa | 210 |
| Poisson's ratio | - | 0.31 |
| fracture toughness | MPa m1/2 | 8-10 |
| thermal expansivity | [normal temperature～400℃] x10-6 | 10.3 |
| Thermal conductivity | W/(m.K) | 3 |
| nitric acid(90%) | weight loss | 0 |
| sulfuric acid(95%) | 0.03 |
| sodium hydroxide(30%) | 0.07 |
Advantages:
1). Excellent electrical insulation;
2). High hardness;
3). Relatively low strength and fracture toughness;
4). Resistance to wear and corrosive;
5). Excellent thermal stability;
6). Resistance to high temperatures;
7). High electrical resistivity;
8). Good chemical stability and resistance.
More Picture:
Why Choose Us?
1. 5 years of professional production industrial ceramics factory
2. High quality products with low price
3. High precision parts with lowest tolerance
4. Short time for production
5. Has a group of experienced, professional and efficient R&D team
6. Has a good reputation in China and abroad.